Incremental damage development in a 3D woven carbon fibre composite

Biomedical Sciences Research Institute Computer Science Research Institute Environmental Sciences Research Institute Nanotechnology & Advanced Materials Research Institute

King, S, Stewart, G, McIlhagger, AT and Quinn, JP (2007) Incremental damage development in a 3D woven carbon fibre composite. POLYMERS & POLYMER COMPOSITES, 15 (7). pp. 521-533. [Journal article]

Full text not available from this repository.

Abstract

Interest in 3D woven carbon fibre composites has increased within industries such as aerospace, automotive and marine, due to their high strength to weight ratio, their increased tailorability and their capacity to be manufactured into near net shape preforms, thereby reducing parts count, assembly time, labour intensity and costs. It is vital that critical areas of concern such as damage (and in particular damage, initiation and development) are studied and understood, thereby reducing the limiting factors to their acceptance. The damage initiation and subsequent intervals of development for ILSS (Interlaminar Shear Strength) were determined experimentally. Particular focus is paid to the significance of binder edge and binder middle testing and the influence of through-the-thickness (T-T-T) reinforcement in relation to damage types and development. Control samples for binder edge and binder middle loading locations were tested to failure as a means of determining an average point of failure, allowing the generation of testing intervals. The performance and architecture of samples from each incremental interval were characterised using a combination of graphical analysis and optical microscopy with the aid of dye-penetrant to highlight fibre damage and matrix cracking. Samples displayed specific damage initiation points, thus allowing the generation of a damage guide relating to applied force. In addition, the results imply that a relationship exists between the location of applied load and subsequent damage, thus showing the significant influence played by the T-T-T binder loading location on damage development within 3D woven carbon fibre composites.

Item Type:Journal article
Faculties and Schools:Faculty of Computing & Engineering
Faculty of Computing & Engineering > School of Engineering
Research Institutes and Groups:Engineering Research Institute
Engineering Research Institute > Engineering Composites
ID Code:5870
Deposited By:Dr Alistair McIlhagger
Deposited On:18 Jan 2010 11:40
Last Modified:18 Aug 2011 11:52

Repository Staff Only: item control page