Effects of nanoclay and fire retardants on fire retardancy of a polymer blend of EVA and LDPE

Biomedical Sciences Research Institute Computer Science Research Institute Environmental Sciences Research Institute Nanotechnology & Advanced Materials Research Institute

Zhang, J, Hereid, J, Hagen, M, Bakirtzis, D, Delichatsios, M, Fina, A, Castrovinci, A, Camino, G, Samyn, F and Bourbigot, S (2009) Effects of nanoclay and fire retardants on fire retardancy of a polymer blend of EVA and LDPE. FIRE SAFETY JOURNAL, 44 (4). pp. 504-513. [Journal article]

Full text not available from this repository.

DOI: 10.1016/j.firesaf.2008.10.005

Abstract

The effects of nanoclay (organoclay) and fire retardants (aluminium tri-hydroxide and magnesium hydroxide) on the fire retardancy of a polymer blend of ethylene-vinyl acetate (EVA) and low-density polyethylene (LDPE) were assessed using thermogravimetric analysis (TGA) and the cone calorimeter. TGA measurements were conducted in nitrogen and air atmospheres at different heating rates (1-20 degrees C/min), whilst in the cone calorimeter square samples were tested under various external heat fluxes (15-60kW/m(2)). The TGA results indicate that the nanoclay (NC) alone has little effect on the degradation of the polymer blend, whereas aluminium tri-hydroxide (ATH) and magnesium hydroxide (MH), used as fire retardants (FRs), generally decrease the onset degradation temperature and also reduce the peak mass loss rate. However, it was found in the cone calorimeter that, though having negligible effect on ignition, the nanoclay reduces the heat release rate (HRR), and increases smoke and CO yields. In comparison, FRs (ATH or MH) were found to delay ignition owing to loss of water at lower temperatures, reduce the HRR, and have similar smoke and CO yields compared to the polymer blend. The reduced HRRs for both the nanoclay and FRs can be attributed to the formation of a surface layer (a nano layer for nanoclay and a ceramic-like layer of Al2O3/MgO for FRs), which acts as mass and heat barriers to the unpyrolysed material underneath. The global effect of the surface layer for the polymer blend nanocomposite was examined using a previously developed numerical model, and a methodology for predicting the mass loss rate was subsequently developed and validated. (c) 2008 Elsevier Ltd. All rights reserved.

Item Type:Journal article
Faculties and Schools:Faculty of Art, Design and the Built Environment
Research Institutes and Groups:Built Environment Research Institute
Built Environment Research Institute > Fire Safety and Engineering Research and Technology Centre (FireSERT)
ID Code:3458
Deposited By:Professor Michael Delichatsios
Deposited On:16 Dec 2009 10:19
Last Modified:16 Dec 2009 10:19

Repository Staff Only: item control page