Estimating the Shelf Life of Medical Plastics by Accelerated Ageing

Biomedical Sciences Research Institute Computer Science Research Institute Environmental Sciences Research Institute Nanotechnology & Advanced Materials Research Institute

Dixon, D (2012) Estimating the Shelf Life of Medical Plastics by Accelerated Ageing. Medical Plastics News, 6 . pp. 22-23. [Journal article]

Full text not available from this repository.

URL: http://viewer.zmags.com/publication/ed0696aa#/ed0696aa/55

Abstract

All materials degrade over time, but the effects of ageing on polymers can be particularly dramatic. Just have a look at PVC guttering or black PP car bumpers that have been exposed to the elements for several years, leading to severe embrittlement and bleaching. While ageing occurs more rapidly when polymers are exposed to weathering, ageing is also observed in medical plastic products stored in protective opaque packaging. Several mechanisms are responsible for the typical ageing effects seen in unpigmented polymers of yellowing and a loss in flexibility. This degradation is chiefly caused by UV exposure, oxidative damage and changes to the polymers crystalline structure referred to as physical ageing. Ageing can reduce molecular weight by chain scission, induce crosslinking and modify crytallinity, all of which alter mechanical performance giving rise to the risk of product failure. Polymer ageing can be monitored using a range of analytical methods including thermal analysis, spectroscopy, gel permeation chromatography, density measurements and mechanical tests.

Item Type:Journal article
Faculties and Schools:Faculty of Computing & Engineering
Faculty of Computing & Engineering > School of Engineering
Research Institutes and Groups:Engineering Research Institute
Engineering Research Institute > Nanotechnology & Integrated BioEngineering Centre (NIBEC)
ID Code:22772
Deposited By:Dr Dorian Dixon
Deposited On:09 Jul 2012 16:18
Last Modified:09 Jul 2012 16:18

Repository Staff Only: item control page