Kilpatrick, W, Brown, D, McMurray, R and Leacock, AG (2010) The effect of serrated yielding on the determination of r-values in aluminium alloys and yield locus calibration. Materials Science and Engineering: A, 527 (29-30). p. 7557. [Journal article]
Full text not available from this repository.
This study investigates the effect serrated yielding (Portevin-Le Châtelier effect) has on the determination of the plastic strain ratio (r-value) for the 2024 aluminium alloy. The aluminium alloy specimens were initially in the fully annealed O-condition. The specimens experienced a softening mechanism through a solution heat treatment (SHT) process, followed by an oil quench. The specimens were permitted to recover for periods ranging between 0.5 and 12 h by room temperature (RT) natural ageing before undergoinga uniaxial tensile test along the longitudinal axis to determine the r-value as a function of natural ageing time. The current study reveals the irregular variation in the transverse strain affects the gradient of the longitudinal–transverse strain plot and consequently the r-value. It is demonstrated that the serrated yielding directly influences the Hill 1948 yield locus when calibrated using two r-values and one yield strength for the 2024 aluminium alloy. Serrated yielding results in an underestimation of the plane stress (rolling) of 0.5≤plane stress rolling (MPa)≤5.6, plane stress (transverse) of 1.0≤plane stress transverse (MPa)≤9.2, and biaxial stress of 1.4≤biaxial stress (MPa)≤7.4. It is also shown that serrated yielding occurs after a critical strain of 0.07≤plastic strain≤0.13 and is reduced by natural age hardening. © 2010 Elsevier B.V. All rights reserved.
|Item Type:||Journal article|
|Faculties and Schools:||Faculty of Computing & Engineering|
Faculty of Computing & Engineering > School of Engineering
|Research Institutes and Groups:||Engineering Research Institute|
Engineering Research Institute > Advanced Metal Forming
|Deposited By:||Mrs Ann Blair|
|Deposited On:||08 Nov 2010 09:32|
|Last Modified:||08 Nov 2010 09:32|
Repository Staff Only: item control page